Flattening and solidification of thermally sprayed particles

In this article, molybdenum particles were plasma sprayed on copper, zirconia, and glass substrates. The impact of the molten particles was monitored using a fast two-color optical fiber pyrometer focused on a small spot on the substrate surface. The apparent duration of the flattening process and the cooling speed, both determined from the pyrometer signals, were found to depend on the substrate conditions and to vary with coating thickness. The substrate material and its roughness were also found to influence the texture in the sprayed coatings. Furthermore, a transient thermal flow numerical model was used to compute reliable thermal histories of the impinging particles and the underlying lamellae, the interfacial thermal resistance being determined by comparison of experimental thermograms with computed ones.     

45SiMnCrMo铸钢磨球强韧化的研究

利用Formastor-Digital全自动相变测量仪测定了ZG45SiMnCrMo钢的临界点,研究了该钢的余热淬火温度、回火温度对强韧性的影响和淬硬层分布.结果表明,45SiMnCrMo铸钢采用900℃淬火,300℃回火,强韧性最佳.     

大型风电球墨铸铁件的生产实践

以轮毂为例,介绍对大型风力发电机球墨铸铁件生产工艺进行的试验研究。通过优化铸型工艺,采用适当的浇注系统和低温石墨化退火工艺,选择合理的化学成分,控制球化处理与孕育处理,可生产出各项性能指标合格的风电铸件。     

非晶(Fe_(80)Ni_(20))_(78)Si_(22-x)B_x合金的磁矩与Curie温度

用液态快淬法制备非晶合金条带时,通过加入15—30％的B与Si等类金属含量是形成非晶状态的必要条件。但是,由于Si与B等类金属元素的加入,使非晶态合金的磁性受到明显的影响。本文实验研究了Si与B含量间的相对变化对(Fe_(80)Ni_(20))_(78)Si_(22-x)B_x合金的饱和磁矩、平均原子磁矩与Curie温度的影响关系。利用电子转移模型与分子场近似理论定性的解释了(Fe_(80)Ni_(20))_(78)-Si_(22-x)B_x合金的磁矩(M_s)与Curie温度(T_c)随     

钢铁常温发黑剂在推广中的问题和对策探讨

论述了铜—硒钢铁常温发黑剂在推广中遇到的结合力差、溶液维护困难、产生黄色水锈等问题，研究了对策并提出了改进措施。研制的HD钢铁常温发黑剂和新型防锈钝化水能有效解决上述问题。     

EFFECT OF NaOH CONCENTRATION AND AlO_2~- SPECIES ON CAUSTIC STRESS CORROSION CRACKING OF A LOW ALLOY STEEL AT 260℃

用慢应变速率法（ＳＳＲＴ）、动电位扫描和循环伏安法研究１６ＭｎＲ钢在氧化铝溶出过程中的高温碱脆行为。结果表明，在２６０℃，１６ＭｎＲ钢的碱脆敏感性随ＮａＯＨ浓度（７．４２－１０．０６ｍｏｌ／Ｌ）的升高而增大；当碱液中含有ＡｌＯ２＾－离子时，１６ＭｎＲ钢的碱脆敏感电位区缩小，样品表面腐蚀产物保护性好，ＡｌＯ２＾－离子对低合金钢高温碱脆有一定抑制作用；１６ＭｎＲ钢在２６０℃碱液中生成的腐蚀产物为Ｆｅ３     

Effects of Thermal Exposure on the Tensile and Fatigue Properties of Cast Ti—47Al—2Cr—2Nb--0.15B Alloy

测量了铸造Ti—47Al—2Cr—2Nb-0．15B(原子分数，％)合金的高温疲劳强度以及650℃／100h和800℃／100h热暴露后的拉伸性能和疲劳强度，采用X射线衍射和扫描电镜等方法分析了经热暴露后合金基体组织的变化和表面层的结构．随暴露温度的提高，合金的室温塑性和疲劳强度降低，650℃附近有一转折点，大于650℃时上述性能加速下降；合金高温疲劳性能具有相似的变化规律．显微分析表明，在热暴露或高温疲劳实验时，表面形成的脆性层是导致合金性能降低的直接原因；而随温度的提高，表面层由渗氧层转变为氧化层是导致合金性能随温度变化出现转折的原因．     

氢对Ti合金的Debye温度和晶格常数的影响

使用X射线衍射仪测定出不同氢含量的Ti-30Mo合金的Debye特征温度值以及晶格常数的变化,结果表明随着氢含量的增加,Debye特征温度相应地减小而晶格常数增加,证实了氢含量的增加会导致金属原子间键合力的减弱,从而造成金属脆化。     

高强度钢腐蚀疲劳裂纹扩展的温度效应和过载迟滞效应

通过在18,35和55℃蒸馏水中疲劳裂纹扩展试验,证明了超高强度钢30CrMnSiNi2A腐蚀疲劳具有强烈的温度效应,得到了ΔK值和温度对裂纹扩展速率影响的复合表达式。由于扩展速率数据拟合得到的表观激活能值(36.7kJ/mol)十分接近于氢在γ-Fe中的扩散激活能值,支持了氢助裂纹扩展的观点。对大气中疲劳裂纹扩展具有重要价值的过载迟滞效应,在腐蚀疲劳时显著地减小,在0.1Hz的低频率下尤其明显。     

奥氏体Fe-Mn合金的低温脆性

奥氏体型合金一般具有优良的低温韧性.本文对奥氏体Fe-Mn合金低温变脆现象进行了研究.实验结果肯定了低温下有冷脆倾向;指出随Mn含量增多,冷脆转变温度增高,呈沿晶脆断;发现Mn沿晶界偏聚,且Mn含量愈高偏析程度愈大;初步分析了晶界Mn富集造成冷脆的因素;未能证实前人提到的可能引起低温变脆的-100℃时面心立方→面心四方相变的存在.